Stainless Steel - Grade 310 (UNS S31000

Chemical Formula

Fe, <0.25% C, 24-26% Cr, 19-22% Ni, <2% Mn, <1.5% Si, <0.45% P, <0.3% S

Stainless steel grade 310 bersifat martensitic, dan merupakan material yang sempurna untuk temperature tinggi dan corosif dengan komposisi carbon yang sedikit dan tinggi nikel.

Komposisi Kimia

Table 1. Composition ranges for 310 grade stainless steel

Grade

310

min.

max.

0.25

2.00

1.50

0.045

0.030

24.0

26.0

19.0

22.0

310S

min.

max.

0.08

2.00

1.50

0.045

0.030

24.0

26.0

19.0

22.0

Mechanical Properties

Table 2. Mechanical properties of 310 grade stainless steel

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Rockwell B (HR B) max	Brinell (HB) max
310	515	205	40	95	217
310S	515	205	40	95	217

Physical Properties

Table 3. Physical properties of 310 grade stainless steel in the annealed condition

Grade	Density (kg/m³)	Elastic Modulus (GPa)	Mean Coefficient of Thermal Expansion (μm/m/°C)			Thermal Conductivity (W/m.K)		Specific Heat 0-100^°C (J/kg.K)	Electrical Resistivity (nΩ.m)
			0-100°C	0-315°C	0-538°C	at 100°C	at 500°C
310/S	7750	200	15.9	16.2	17.0	14.2	18.7	500	720

Grade Specification Comparison

Table 4. Grade specifications for 310 grade stainless steel

Grade	UNS No	Old British		Euronorm		Swedish SS	Japanese JIS
Grade	UNS No	BS	En	No	Name	Swedish SS	Japanese JIS
310	S31000	310S24	-	1.4840	X15CrNi25-20	-	SUH 310
310S	S31008	310S16	-	1.4845	X8CrNi25-21	2361	SUS 310S